Resources Recycling ISSN:2765-3439(Print) 2765-3447(Online) 자원리싸이클링

Sulphuric acid (H₂SO₄) leaching and hydrolysis were experimented for the recovery of titanum dioxide (TiO₂) from the water-leached residue followed by soda-roasting spent SCR catalysts. Sulphuric acid leaching of Ti was carried out with leachate concentration (4~8 M) and the others were fixed (temp.: 70 ℃, leaching time: 3 hrs, slurry density: 100 g/L, stirring speed: 500 rpm). For recovering of Ti from the leaching solution, hydrolysis precipitation was conducted at 100 ℃ for 2 hours in various mixing ratio (leached solution:distilled water) of 1:9 to 5:5. The maximum leachability was reached to 95.2 % in 6 M H₂SO₄ leachate. on the other hand, the leachability of Si decreased dramatically 91.7 to 3.0 % with an increase of H₂SO₄ concentration. Hydrolysis precipitation of Ti was proceeded with leaching solution of 8 M H₂SO₄ with the lowest content of Si. The yield of precipitation increased proportionally with a dilution ratio of leaching solution. Moreover, it increased generally by adding 0.2 g TiO₂ as a precipitation seed to the diluted leaching solution. Ultimately, 99.8 % of TiO₂ can be recovered with the purity of 99.46 % from the 1:9 diluted solution.