The hydrogen reduction behavior of molybdenum oxides was studied using a horizontal-tube reactor. Reduction was carried out in two stages: MoO₃ → MoO₂ and MoO₂ → Mo. In the first stage, a mixed gas composed of 30 vol% H₂ and 70 vol% Ar was selected for the MoO₃ reduction because of its highly exothermic reaction. The temperature ranged from 550 to 600 °C, and the residence time ranged from 30 to 150 min. In the second step, pure H₂ gas was used for the MoO₂ reduction, and the temperature and residence time ranges were 700–750 °C and 30–150 min, respectively. The hydrogen reduction behavior of molybdenum oxides was found to be somewhat different between the two stages. For the first stage, a temperature dependence of the reaction rate was observed, and the best curve fittings were obtained with a surface reaction control mechanism, despite the presence of intermediate oxides under the conditions of this study. Based on this mechanism, the activation energy and pre-exponential were calculated as 85.0 kJ/mol and 9.18 × 10⁷, respectively. In addition, the pore size within a particle increases with the temperature and residence time. In the second stage, a temperature dependence of the reaction rate was also observed; however, the surface reaction control mechanism fit only the early part, which can be ascribed to the degradation of the oxide crystals by a volume change as the MoO₂ → Mo phase transformation proceeded in the later part.