Sericite was ground with or without additives (LiNO₃ or TiO₂) using a planetary mill. The resultant ground products included the average particle size of 2-3 μm (sericite only or sericite+LiNO₃) and 0.5-0.6 μm (sericite+TiO₂) were obtained within 10 minutes of grinding time. respectively. In the grinding of the sericite without any addictive, the particle size initially decreased, but, as grinding time elapsed thereafter, agglomerates were formed and D50 increased over 10 μm. In contrast, when the additive was added, the particle size decreased as the grinding time elapsed and any aggregation was relatively not noticeable, compared with the grinding of the sericite only. As a result of measuring the zeta potential for the raw or the ground samples, variation of the zeta potential values according to pH at the early stage of the grinding with the addictives was gentler than that at the final stage of grinding, which showed the relatively similar trend to the pH-zeta potential correlation in grinding of raw sericite. In addition, as a result of the disintegration experiment through ultrasonic excitation, D50 decreased rapidly only until the disintegration time of about 50 minutes.